China mold and die makers,China mold supplier,mold and die makers,mold supplier
 
样板工程 Product list more
  ICON  Mould Samples
  ICON  Plastic Products
        Auto Parts Mould
        Commodity Mould
        Furniture Parts
        Electronics,Electrical parts
        Double Coloured Molding parts
        Transparent parts
        Threaded Parts
        Plastic Pallets
        Pipe Fitting Parts
        Medical Device
        Turnover Box Mould
  ICON  Zinc Alloy Products
  ICON  Aluminum Alloy Products
 
样板工程 Contact us more

Factory Address:No.5 unit 2 Lane, Maiyuan Road, Xinan District, Changan Town, Dongguan City, Guangdong, China.
Tel: +86-769-82387016  
Fax: +86-769-82387081    
Marketing:carry@hafo-mould.com
Engineering:cora@hafo-mould.com 

 

产品展示 Current location:Home > News
Making the Right Mold Material Selection for Thermal Management of Molds and Inserts
作者: 发布于:2014-3-4 10:59:51 点击量:

In plastic injection molding, the performance of the heat transfer from the molten plastic to the cooling media through the mold determines the cost-effectiveness of the process. For a given application, understanding the mechanism of heat transfer in different zones of the mold is necessary to design and ultimately build an effective tool.

On one hand, this allows for optimization of the cooling system configuration. On the other hand, it helps with selecting the right material for the mold and/or for the different zones of the mold in order to optimize cooling time and minimize scrap due to warpage or under-fill.

In addition to the thermal requirements, mold materials need to respond to mechanical and tribological demands of the mold, which may vary throughout the tool geometry.
The thermal properties of the mold play an important role in improving the heat transfer from the molten plastic through the mold and in reducing cooling time—locally or generally.

For several decades now, the thermal conductivity of conventional tool steels used for plastic injection molding has been limited to 12-20 Btu/(hr•ft⋅°F), the lower range corresponding to tool steels presenting higher mechanical and tribological properties. However, tool steels that provide thermal conductivity up to 35 Btu/(hr•ft⋅°F) , commercially known as high thermal conductivity steels (HTCS), should be considered.

Two grades of these tool steels, HTCS-1 and HTCS-2, have been used for plastic injection molding. Both present thermal conductivities of more than 35 Btu/(hr⋅ft⋅°F) (see Figure 1), while the mechanical properties are close to those of conventional hot-work tool steel H13. HTCS-2 is a remelted tool steel with a high degree of polishability, and HTCS-1 is a powder metallurgy tool steel with moderate polishability but very high abrasive wear resistance. The latter grade can be used for molds that present problems with abrasive wear (plastic reinforced with fiber glass), which do not require a very high degree of polishability.

Moldmakers and component producers looking to optimize the thermal management of the mold, process productivity and tool durability while molding plastic components reinforced with abrasive fiber glass should consider these tool steels.

A promising feature of these tool steels is that they can reach a hardness level of more than 50 HRC while maintaining a very high thermal conductivity, making them candidates for not only tackling thermally related problems (for example, productivity, part warpage, poor temperature distribution, cooling, etc.), but also mold durability, especially when the plastic is reinforced with abrasive glass fibers.  

Figure 2 shows that the best compromise between mold durability and cycle time for an electrical connector (example supplied by STM Stahl) was a mold made of HTCS-2 (compared with H11 steel and a copper-based alloy).
 
These high thermal conductivity steels have also been applied in molds where poor distribution of the temperature over the surface of the mold generates warpage and filling problems. This is because the high thermal conductivity also indicates a high diffusivity of heat through the mold in all directions. So, for difficult mold geometries, especially larger molds, a good distribution may be obtained when using high thermal conductivity steels. As for size, molds or inserts of 47" × 32" × 39" and larger can be produced with these tool steels.

Figure 3 shows a high-volume electrical box. In this application with conventional tool steels, the rate of scrap occurrence was very high due to the warpage produced from bad temperature distribution over the mold surface. This problem was solved by switching to HTCS-1.

Summary
The very high thermal conductivity of these tool steels enable them to be used to tackle long cycle times, poor temperature distribution and mold durability in plastic injection molding, especially for fiberglass-reinforced plastics. The grades presented here are candidates for mold designers and moldmakers to consider using when dealing with the thermal problems of the mold and to improve the cost-effectiveness of the process. For plastic injection molding, these grades can be used to build complete molds as well as to build big and small inserts with all the hardness levels required for various applications.